Abstract

The mechanical properties of carbon fiber reinforced polymer composites depend upon fiber-matrix interfacial properties. In this investigation to improve the mechanical properties of polymer composites, graphene oxide was used as one of the filler for the development of carbon fiber/graphene oxide-epoxy hybrid composites. Initially, epoxy resin was modified by incorporating different weight% of graphene oxide from 0.1 to 0.6 wt%. The desired size of carbon fiber fabric was impregnated with modified epoxy resin to develop hybrid composites by compression molding technique. The graphene oxide synthesized was characterized by various techniques such as FTIR, XPS, NMR, XRD and Raman Spectroscopy. It is observed that graphene oxide synthesized possesses different type of functional groups which are responsible for making interactions with epoxy resin and Carbon fibers. The hybrid composite flexural strength increases by 66%, flexural modulus by 72%, while interlaminar shear strength (ILSS) increases by 25% at 0.3 wt% of graphene oxide included in the carbon fiber reinforced polymer hybrid composites. The enhancement in the properties of composites at the percolation threshold of graphene oxide is due to hydrogen type bonding and mechanical interlocking of graphene oxide with carbon fibers and epoxy resin. The graphene oxide utilization is one of the approaches for improving the properties of carbon fiber polymer composites.

4. Conclusions

The carbon fiber-graphene oxide epoxy resin based composites demonstrate the excellent mechanical properties on inclusion of GO in an epoxy matrix. The bending strength increases by 66% and modulus by - 70% at only 0.3 wt% of GO. The interlaminar shear strength increases by 25%. The increase in mechanical properties is due to the improvement in properties of epoxy resin and interfacial interaction between reinforcement and matrix by hydrogen bonding and mechanical interlocking of graphene oxide as well. The high surface area of nanosize GO makes better bonding around the reinforcements at the very small content of GO and higher content of GO results in to the agglomeration in the matrix phase which ultimately around the fibers. The graphene oxide utilization is one of the approaches for improving the properties of carbon fiber polymer composites.